多孔酚醛树脂固载铑膦配合物催化剂的制备与催化性能研究
Preparation and catalytic performance of the immobilized rhodium-phosphine complexes over porous phenolic resin
投稿时间:2017-12-22  修订日期:2018-03-19
DOI:
中文关键词: 酚醛树脂  均相催化剂固载化  铑膦配合物  氢甲酰化
英文关键词: phenolic resin  immobilization catalyst  rhodium-phosphine complexes  hydroformylation
基金项目:国家自然科学基金项目(面上项目,重点项目,重大项目)
作者单位E-mail
钱子隆 福州大学石油化工学院 qianzilong77@qq.com 
周聪 福州大学石油化工学院  
赵素英 福州大学石油化工学院  
吴丹 福州大学石油化工学院 wudan@fzu.edu.cn 
摘要点击次数: 19
全文下载次数: 13
中文摘要:
      以多孔酚醛树脂XAD761为载体,采用表面官能团修饰的方法制备了固载铑膦配合物的催化剂XAD761/P/Rh,实现了均相氢甲酰化反应催化剂的固载化。采用红外光谱和等温氮气吸附等方法对所制得的催化剂进行表征,证实了二苯基氧磷结构配位中心的存在及铑膦配合物催化中心在酚醛树脂载体表面的形成。经过电感耦合等离子-原子发射光谱测得磷和铑的负载量分别为1.39%和0.40%,催化剂中磷铑比为11.5。分别以1-辛烯和苯乙烯为底物考察了催化剂的催化性能,结果表明,在一定条件下XAD761/P/Rh在催化活性方面和三苯基膦作配体时的均相催化剂效果相当,1-辛烯的和苯乙烯的成醛收率分别可以达到77.9%和99.6%。所制备的催化剂经过简单的过滤分离即可实现循环使用。
英文摘要:
      XAD761 / P / Rh catalyst was prepared by the modification of the surface functional groups over the porous phenolic resin XAD761, and the immobilizd of homogeneous hydroformylation catalyst was obtained. The prepared catalyst was characterized by the infrared spectrum and the isothermal N2 adsorption to confirm the existence of the coordination center of diphenyloxide and the formation of the catalytic center of rhodium-phosphine complex on the surface of the phenolic resin. The analysis data from the inductively coupled plasma-atomic emission spectrometry showed that the loadings of phosphorus and rhodium were 1.39% and 0.40%, respectively, and the ratio of phosphorus to rhodium in the catalyst was 11.5. The catalytic performance of the prepared catalyst was investigated by the hydroformylation reaction of 1-octene and styrene. The results showed that the activity of XAD761/P/Rh catalyst was similar with the homogeneous catalyst with the triphenylphosphine as ligand, the yield of aldehydes could reach 77.9% and 99.6% for 1-octene and styrene, respectively. The prepared solid catalyst could be easily recycled through filtration.